Name: Raw Chloroprene Rubber Neoprene Polychloroprene Cr244 for Universal Glue
Brand: Madeinchina.com
SKU: MIC-1254698
Price: 1680.00 USD
Availability: InStock

Raw Material:

Synthetic Rubber

Material:

Crepe Rubber

Appearance:

Granules

Quality:

Industrial

Sample:

Free Sample

Certificate:

ISO9001

Delivery Time:

3-5 Days

Production:

30000kg/Month

Supply Type:

OEM/ODM

Tensile Strength,MPa:

Modulus at 500%,MPa:

1-5

Elongation at Break, %:

750

Volatile Matter, %,Max:

1.5

Ash Content, %,Max:

1.5

Trademark:

JTC

Transport Package:

25kg Bag/Carton/Drum

Origin:

China

HS Code:

291830009

Product Description

Polychloroprene Rubber Cr232 122

Item		Index
Item		Grade A	Grade B	Grade C
Viscosity in 15% solution, mPa.	CR2441	1000-3000	1000-3000	1000-3000
	CR2442	3001-7000	3001-7000	3001-7000
	CR2443	7001-10000	7001-10000	7001-10000
Peel strength, N/cm ≥		90	80	75
Volatile matter , %≤		1 . 0	1 . 2	1 . 2
Ash content , %≤		1 . 0	1 . 2	1 . 2

Item		Index
Item		I	II
Viscosity in 15% solution, mPa.	CR248	1000-3000	3001-6000
Peel strength, N/cm ≥		70	70
Volatile matter , %≤		1 . 2	1 . 2
Ash content , %≤		1 . 2	1 . 2

Item		Index
Item		Grade A	Grade B	Grade C
Mooney viscosity ML1001+ 4 ºC	CR2441	30-45	30-45	30-45
	CR2442	46-60	46-60	46-60
Tensile strength MPa35min ≥		26	22	20
500% Stressatdefiniteelongation MPa ≥		1-5	1-5	1-5
Tensile stretch,% ≥		800	780	750
Volatile matter , %≤		1 . 0	1 . 2	1 . 2
Ash content , %≤		1 . 0	1 . 2	1 . 2

Type	Grade	Mooney Viscosity		Crystallization Rate	Characteristics
General	CR121	CR1211	30-45	Medium	Good tear and flexural resistance
		CR1212	46-60
	CR232	CR2321	35-45		Good weatherability, high loading
		CR2322	46-55
		CR232 High Viscosity	According to customers' requirement
	CR322	CR3221	30-45		Good tear resistance and excellent dynamic mechanical properties
		CR3222	46-60

Price	$1680.00
Min Order	1 Ton