Product Description
Material(s) Description
Warp material: Polyester
Weft material: Irradiated, modified polyolefin
Coating: Modified polyolefin
Operating temperature range (3000 hours): -40°C to 125°C
Operating temperature range (1000 hours): -40°C to 150°C
Minimum recovery temperature: 110°C
Recommended recovery temperature: 150°C to 200°C
Maximum storage temperature: 50°C
Standard: TL52668 TL52361 D44 1959 GMW14327
Testing organization: CTI PONY
| Product description (CL-KSD) | Inside diameter (mm) | |
| D (min. ) expanded as supplied | D (max. ) recovered after heating | |
| Φ6/3-B | 6 | 3 |
| Φ8/4-B | 8 | 4 |
| Φ10/5-B | 10 | 5 |
| Φ12/6-B | 12 | 6 |
| Φ16/8-B | 16 | 8 |
| Φ20/10-B | 20 | 10 |
| Φ25/12-B | 25 | 12 |
| Φ30/15-B | 30 | 15 |
| Φ35/17.5-B | 35 | 17.5 |
| Φ40/20-B | 40 | 20 |
| Φ50/25-B | 50 | 25 |
| Φ60/30-B | 60 | 30 |
| Φ70/35-B | 70 | 35 |
| Φ80/40-B | 80 | 40 |
| Φ100/50-B | 100 | 50 |
| B: Black | ||
| Other specifications can be customized | ||
| Property | Test condition(s) | Performance |
| Thermal ageing | 168 hrs at 125°C | No deterioration in abrasion resistance at 23°C |
| 24 hrs at 125°C | No deterioration in abrasion resistance at 23°C | |
| Flammability | MVSS 302 | Burning rate≤100 mm/min |
| Low temperature flexibility | 4 hours at -40°C, 10X diameter mandrel | No cracking |
| Abrasion resistance (1.5N load, 0.3mm radius metal blade, 60 cpm, 50mm stroke, 144 000 cycles) | Environmental Chamber Temperature: -35°C | No wear to underlying rubber hose |
| Environmental Chamber Temperature: 140ºC | ||
| Temperature resistance 1) Test temperature 140 ºC, for 500 hours 2) Remove the sample and cool it to room temperature...Then place the sample at -35°C for 22 hours. 3) Then bend the sample 180 degrees around a cylinder with a radius of 30mm | Test temperature 140 ºC, for 500 hours | The protection tube is not damaged Standard: TL52668 |