Product Description
JHSW8809 Two Components Brushable Aromatic Manual Polyurea is originally designed to where big machine is not allowed to go in and some small area repairing projects. The system consists of A component, a quasi-prepolymer rich of free NCO, and B component, a mixture of polyetheramines, amine extenders and other additives. JHSW8809 has good adhesion, good elasticity, bright and smooth paint film, excellent wear-resisting performance and insensitivity to moisture. It can be constructed by manual scraping don't need high pressure machine. Advantages:
- Excellent Physiochemical Properties
- Bondable and paintable to various kinds of substrates
- Ambient insensitive, good thermal stability
- 100% Solids, No VOC's, Odorless, No Toxic Vapors
- Good resistance to a wide range of chemical attack
- Excellent Anti-corrosion and Waterproof Properties
- Seamless, flexible, slick and non-porous
JHSW8809 two components manual polyurea material is mainly used in some large-area projects that are not easy to spray construction. It is used as a substitute product for spraying polyurea elastomer. It can also be used as a local repair material after spraying polyurea elastomer material damage.
| Tensile Strength /MPa | ≥16 | Solids Content/% | ≥99 |
| Elongation/% | ≥400 | VOC | 0 |
| Tear Strength/( N/mm) | ≥50 | Tack Free Time/h(25ºC,RH=60%,h) | ≤2 |
| Shore Hardness | ≥85A | Recoat windew/ h(25ºC,RH=60%,h) | 24h |
| Adhesion /(Pull off, concrete,MPa) | ≥2.5 | Pot Life/ h(25ºC,RH=60%,min) | 20-30 |
| Density/( g/cm3) | 0.95~1.05 | Shelf Life | 12 months, unopened at 0~40 ºC |
| Abrasion Resistance /(GB/T 1689-1998, cm3/1.61km, g) | ≤0.04 | Flash Point/ ºC | >100 |
| Impermeability(0.3MPa/30min) | Impervious | Mix Ratio V/V | 5: 1 or 4:1 |
| Chemical Resistance | No corrosion, No Blister, No Spalling | Colors: | clear or Optional |