Tungsten ball with band
Aviation, Industrial, Defense
ASTM, AMS-T-21014
90%~97%
Alloy
Round
Sphere
Sintered (with Band); Grind (Without Band)
ASTM B777, AMS-T-21014
1, 2, 3, 4
16.85~17.25, 17.15~17.85, 17.75~18.35, 18.25~18.85
90, 92.5, 95, 97
32HRC, 33HRC, 34HRC, 35HRC
758MPa, 724MPa, 689MPa
517MPa
5%, 3%, 2%
Tungsten Bearing Ball
Ball
Grinding Ball
Sintered Ball with Band
Kefeng
Export Wooden Cases or Iron Barrels
Dia. 1.5mm~Dia. 380mm
China
81019910
Product Description
Hello, greeting from Xi'an Kefeng Powder Metallurgy Co., Ltd, as a manufacturer, we are welcome you visit our homepage, there are many tungsten alloy high density products, tungsten alloy is one of our products, below I will introduce Tungsten Based high density alloy ball, please see below:
Tungsten alloy ball:
There are three surface we can supply:
1) Sinter ball, with band, no grinding, This ball just sintered, that is to say no grinding, no machined. After sintered, then inspection. Mix-Pressing-Sinter-Inspection-Packing-Shipping.
2) Grinding surface: After sintered, then, grind the ball, surface is 1.6um. MiX-Pressing-Sinter-Inspection-Packing-Shipping
3) Rolling ball: This ball, which is rolled, surface is rough, tolerance is larger than sintered surface and grinding surface.
4) Machined big ball: This ball is bigger, sizes are large, after sintered, need machine, surface usually 3.2um, we can do around dia300mm ball.
Name: Tungsten alloy balls and spheres
Composition: W content: 90-97%,W-Ni-Fe,W-Ni-Cu
Density: 16.85~18.85g/cm3
Standard: AMS-T-21014 and ASTM-B-777
Supply state: Sintered with band or grind surface
Package: 5kgs in polybag, 20kgs in export cases (Wooden cases or Iron Drums)
Payment: Usually T/T and L/C, D/A can be accepted.
Technical parameters
Tungsten alloy ball:
There are three surface we can supply:
1) Sinter ball, with band, no grinding, This ball just sintered, that is to say no grinding, no machined. After sintered, then inspection. Mix-Pressing-Sinter-Inspection-Packing-Shipping.
2) Grinding surface: After sintered, then, grind the ball, surface is 1.6um. MiX-Pressing-Sinter-Inspection-Packing-Shipping
3) Rolling ball: This ball, which is rolled, surface is rough, tolerance is larger than sintered surface and grinding surface.
4) Machined big ball: This ball is bigger, sizes are large, after sintered, need machine, surface usually 3.2um, we can do around dia300mm ball.
Name: Tungsten alloy balls and spheres
Composition: W content: 90-97%,W-Ni-Fe,W-Ni-Cu
Density: 16.85~18.85g/cm3
Standard: AMS-T-21014 and ASTM-B-777
Supply state: Sintered with band or grind surface
Package: 5kgs in polybag, 20kgs in export cases (Wooden cases or Iron Drums)
Payment: Usually T/T and L/C, D/A can be accepted.
Technical parameters
Tungsten heavy alloy | WNiFe (ASTM B777, AMS-T-21014) | WNiCu (ASTM B777, AMS-T-21014) | |||||
| Designation | 90W | 93W | 95W | 97W | 90W | 93W | 95W |
| Density g/cm3) | 16.85~17.30 | 17.15~17.85 | 17.75~18.35 | 18.25~18.85 | 16.85~17.30 | 17.15~17.85 | 17.75~18.35 |
| Tensile Strength (MPa) | 758Min | 758Min | 724Min | 689Min | 648Min | 648Min | 648Min |
| Elongation (%) | 5Min | 5Min | 3Min | 2Min | 2Min | 2Min | 1Min |
| Hardness (HRC) | 32Max | 33Max | 34Max | 35Max | 32Max | 33Max | 34Max |
| Yield strength(MPa) | 517Min | 517Min | 517Min | 517Min | 517Min | 517Min | 517Min |