Product Description
| Type | Rolling Wire |
| Material | 500MPa grade carbon steel wire |
| Flux Containing | Not Containing Flux |
| Extended Length: | >20mm |
| Shielding Gas | CO2 |
| Sep | 0.8, 1.0, 1.2,1.6 |
| Rm/MPa | 490-670 |
| ReL/Rp0.2MPa | >=420 |
| sports event | tensile strength Rm/MPa | yield strength ReL/Rp0.2MPa | elongation A% |
| standard value | 490-670 | >=420 | >=20 |
| example value | 560 | 450 | 26 |
Uses: Our top-tier Honglu Welding Wire is adept at tackling welding tasks across a range of strength-level carbon steels and low alloy steel structures. This versatile solution is ideal for industries such as construction machinery, shipbuilding, vehicle manufacturing, and petrochemical sectors. Ensure robust and reliable welds with our premium welding solution.
Characteristics: The HH-50S-6 wire presents a superior solution for 500MPa carbon steel welding, utilizing CO2 gas shielded welding to minimize spatter while ensuring beautifully shaped welds. Experience high deposition efficiency with minimal porosity sensitivity. Enjoy the advantage of an all-position welding process that consistently delivers exceptional results.
Mechanical properties of the molten metal:(CO2)
| sports event | C | Mu | Si | S | P | Ni | Cr | Mo | V | Cu |
| standard value | 0.06-0.15 | 1.40-1.85 | 0.80-1.15 | <=0.025 | <=0.025 | <=0.15 | <=0.15 | <=0.15 | <=0.03 | <=0.50 |
| example value | 0.08 | 1.50 | 0.89 | 0.012 | 0.013 | 0.03 | 0.02 | 0.002 | 0.003 | 0.11 |
1. Prior to welding, it is crucial to thoroughly eliminate rust, oil, water, and any impurities on the weldment to prevent defects and achieve optimal results.
2. The energy of the welding wire is a critical factor affecting the weld's mechanical properties. For structural components of greater importance, it is advisable to use smaller wire energy to ensure enhanced integrity and performance.