Product Description
1. Product description
2 features
3.product application place :
4.Product test effect display
2 features
3.product application place :
4.Product test effect display
5. Shipping & package : customized package is accepted
Packaging Details
1. Paint is Pour into bucket and cover the bucket tight;
2. Buckets are put one by one closely with rope to bind together tightly
3. Wrapped by shrink film 3 times with pallets under;
4. Loaded by FCL/ LCL container;
6.Company profile:
7. Product Data
| Polyaspartic Garage Floor Top Coating Data Sheet | |||
| Product Name | Polyaspartic Garage Floor Coating- Type A (T23090189) | ||
| Main Raw Material | Polyaspartic polyurea resin | ||
| No# | Project | Data | |
| 1 | Drying time | surface dry | 2H, can be walked by people |
| full dry | 3 days ,Also affected by local temperature | ||
| 2 | Tensile strength (500±50) mm/min,MPa | 21.89 | |
| 3 | Elongation at break (500±50) mm/min,% | 525 | |
| 4 | Tearing strength (500±50) mm/min,N/mm | 78 | |
| 5 | Bending at low temperature | -35ºC, no cracks | |
| 6 | Impermeability | 0.3MPa,120min, No permeability | |
| 7 | Water absorption rate % | 1.9 | |
| 8 | Bond strength (Under standard experimental conditions, MPa) | 3.20 (Substrate Failure ) | |
| 9 | Acid treatment (2% H2SO4 solution 7d) | Tensile strength retention rate % | 77 |
| Elongation at break % | 632 | ||
| Bending at low temperature | -30ºC,no cracks | ||
| 10 | Alkaline treatment 0.1% NaOH solution +saturated Ca(OH)2 solution ,7d | Tensile strength retention rate % | 78 |
| Elongation at break % | 598 | ||
| Bending at low temperature | -30ºC,no cracks | ||
| 11 | Salt treatment (3%NaCI solution ,7d) | Tensile strength retention rate % | 79 |
| Elongation at break % | 603 | ||
| Bending at low temperature | -30ºC,no cracks | ||
| 12 | Artificial climate aging (2745h) | Apperance | No cracks |
| Tensile strength retention rate % | 92 | ||
| Elongation at break % | 567 | ||
| Bending at low temperature | -30ºC,no cracks | ||
| 13 | Water resistance (indoor temperature 14d ) | No cracks, no layering, no sticking, no foaming, no breakage | |
| 14 | Wear resistance (750g/500r) ,mg | 14 | |
| 15 | Impact resistance,1.0kg.m | No damage | |
| Shanghai Juneso New Materials Co.,Ltd | |||