S1000
Photodegradable
9002-86-2
[-CH2-Chcl-]N
618-338-8
Polyvinyl Chloride/PVC
General Plastics
Thermoplastic Plastics
Film Pressure
White
66-68
970-1070
Sheet, Artificial Leathers
White Powder
1 Ton
Qilu
in 25kg/Bag
China
3902100090
Product Description
Items | SG8 | SG7 | SG5 | SG3 |
Average degree of polymerization | 650-740 | 750-850 | 980-1080 | 1250-1350 |
K value | 55-59 | 60-62 | 66-68 | 71-72 |
Viscosity | 73-86 | 87-95 | 107-118 | 127-135 |
Foreign Particle | 16max | 16max | 16max | 16max |
Volatile Matter,% | 30max | 30max | 30max | 30max |
Apparent Density,g/ml | 0.53min | 0.53min | 0.48min | 0.48min |
0.25mm Sieve Retained,% | 2.0max | 2.0max | 1.0max | 1.0max |
0.063mm Sieve Retained,% | 97min | 97min | 95min | 98min |
No.of Grain/400cm2 | 20max | 20max | 10max | 10max |
Plasticizer absorption of 100g resin,g | 14min | 16min | 25min | 28min |
Whitene S S Degree 160 ºC 10min,% | 80 | 80 | 80 | 80 |
Residual Chlore Thylene Content,mg/kg | 1 | 1 | 1 | 1 |
PVC is a linear thermoplastic resin produced by polymerization of vinylchloride monomer. Due to the difference of raw materials, there are two methods of synthesizing vinylchloride monomer - calciumcarbide process and petroleum process. The product has good chemical corrosion resistance, excellent electrical insulation property and fine chemical stability. With highchlorine content, the material has good fire retardance and self-extinguishing properties. PVC is easy to process by extrusion, injection molding, calendering, blow molding, compressing, cast moulding and thermal molding, etc.