Product Description
PVDF resin for LITHIUM BATTERY
It is a powdery polyvinylidenefluoride homopolymerwith low melt mass flow rate and high molecular weight, soluble in polar organic solvents, with high viscosity and adhesive property.
It can be used as a binder for power batteries, energy storage, digital and other lithium batteries. Its high purity and crystallinityguarantee its long-term and stable tolerance in electrolyte.
It is a powdery polyvinylidenefluoride homopolymerwith low melt mass flow rate and high molecular weight, soluble in polar organic solvents, with high viscosity and adhesive property.
It can be used as a binder for power batteries, energy storage, digital and other lithium batteries. Its high purity and crystallinityguarantee its long-term and stable tolerance in electrolyte.
| No. | Properties | Unit | Typical Value | TEST Method |
1 | Solubility | - | Clear and transparent, solution without impurities | 30ºC/1h |
2 | Water content | % | ≤0.10 | ASTM D2902 |
3 | Melting Point | ºC | 162~168 | ASTM D3418 |
| 4 | Crystallinity | % | 38-50 | GB/T 19466.3 |
| 5 | Rotational Viscosity | mPa.s | 9000-15000 | 0.1g/g NMP |
| 6 | Intrinsic viscosity | 10²ml/g | 1.0-2.0 | GB/T 1632.1 |
| 7 | average molecular weight | Da | 800000~1200000 | GPC |
| 8 | Particle size D50 | μm | 1.0-50.0 | GB/T19077 |
9 | Cr | ppm | ≤10 | ICP-OES |
10 | Mn | ppm | ≤10 | |
11 | Fe | ppm | ≤10 | |
12 | Co | ppm | ≤10 | |
13 | Ni | ppm | ≤10 | |
| 14 | Cu | ppm | ≤10 | |
| 15 | Zn | ppm | ≤10 | |
16 | Infrared matching | % | ≥95 | GB/T21186 |