Product Description
HD-4060 / HD-1900
:,
Characteristics: mid density & low hardness
:
Application: casual shoe and lady shoe soles
Typical properties of PU resin
*POLYOL: HD-4060/Cat./H2O/Hardener =220kg/3.2 kg/600g/2 kg
Product Performance
Reactivity
:,
Characteristics: mid density & low hardness
:
Application: casual shoe and lady shoe soles
Typical properties of PU resin
Sample | Appearance | Density (g/cm3@25oC) | Viscosity (mPa·s@40oC) | Package Size (kg/drum) |
| HD-4060 | Clear viscous liquid or waxy solid | 1.13~1.18 | 1900~2400 | 220 |
| HD-1900 | Colorless or pale yellow liquid | 1.18~1.20 | 400~700 | 235 |
Product Performance
| Items | Unit | Value | Test Standard |
| Density | g/cm3 | 0.38-0.45 | GB/T 4472-2011 / DIN 53479 |
| Hardness | Shore A | 40-50 | HG/T 2489-2007 / DIN 53505 |
| Tensile Strength | MPa | >4 | GB/T 10654-2001 / DIN 53504 |
| Elongation | % | >350 | GB/T 10654-2001 / DIN 53504 |
| Angle tear strength | kN/m | >20 | GB/T 529-2008 / DIN ISO 34-1 |
| Flexing | cycle | 100000 | HG/T 2411-2006 / DIN 53578 |
| Abrasion | mm3 | <200 | GB/T 9867-2008 / DIN 53516 |
Reactivity
| Test Items | Unit | Value |
| Ratio of (P+C) and I component | - | 100/88~90 |
| Material temperature | oC | A:40~45 / B:38~42 |
| Cream time | s | 8~10 |
| End of rise time | s | 45~55 |
| Pinch time | s | 100~120 |
| Free rise density | /g/cm3 | 0.25~0.28 |
| Metal mold temperature | oC | 45~55 |
| Demould time | min | 3~4 |
,.
- (,).
.