PPH-T03
Polymer
9003-07-0
(C3h6)N
202-316-6
Polypropylene/PP
General Plastics
Thermoplastic Plastics
Extrusion
White
PE Bag
25kg bag
China
3902100090
Product Description
Description:
Polypropylene(PP) , a kind of non-toxic,odorless, tasteless opalescent polymer with high crystallization, the melting point among 164- 170C, the density among 0.90-0.91g/cm3 , the molecular weight is about 80,000- 150,000. PP is one of the lightest plastic of all varieties at present, particularly stable in water, with a water absorption rate in water for 24 hours is only 0.01%.
Application:
Polypropylene L5E89 adopts the Unipol gas-phase fluidized bed process of US Grace, it is widely be used to produce woven bags, fiber,
applicable for textile,jumbo bags,carpet and backing etc.
Packaging:
In 25kg bag, 16MT in one 20fcl without pallet or 26-28MT in one 40HQ without pallet or 700kg jumbo bag, 26-28MT in one 40HQ without pallet.
Polypropylene(PP) , a kind of non-toxic,odorless, tasteless opalescent polymer with high crystallization, the melting point among 164- 170C, the density among 0.90-0.91g/cm3 , the molecular weight is about 80,000- 150,000. PP is one of the lightest plastic of all varieties at present, particularly stable in water, with a water absorption rate in water for 24 hours is only 0.01%.
Application:
Polypropylene L5E89 adopts the Unipol gas-phase fluidized bed process of US Grace, it is widely be used to produce woven bags, fiber,
applicable for textile,jumbo bags,carpet and backing etc.
Packaging:
In 25kg bag, 16MT in one 20fcl without pallet or 26-28MT in one 40HQ without pallet or 700kg jumbo bag, 26-28MT in one 40HQ without pallet.
| No. | ITEM | UNIT | INDEX | TEST METHOD |
| 01 | Melt mass flow(MFR) Standard value | g/10min | 3.5 | GB/T 3682. 1-2018 |
| 02 | Melt mass flow(MFR) Deviation value | g/10min | ± 1.0 | GB/T 3682. 1-2018 |
| 03 | Color Pellet | Per/kg | ≤30 | SH/T 1541-2006 |
| 04 | Black Pellet | Per/kg | 0 | SH/T 1541-2006 |
| 05 | Dust | %(m/m) | ≤0.05 | GB/T 9345. 1-2008 |
| 06 | Tensile yield stress | Mpa | ≥ 29.0 | GB/T 1040.2-2006 |
| 07 | Tensile fracture stress | Mpa | ≥ 15.0 | GB/T 1040.2-2006 |
| 08 | Tensile fracture nominal stress | % | ≥ 150 | GB/T 1040.2-2006 |
| 09 | Yellow color Index | % | ≤ 4 | HG/T 3862-2006 |