Product Description
A three-way catalytic converter (TWC) is the most important external purification device installed in the automobile exhaust system. It can convert harmful gases such as carbon monoxide (CO), hydrocarbons (HC), and nitrogen oxides (NOx) emitted from the automobile exhaust into harmless carbon dioxide, water, and nitrogen through oxidation and reduction.
Meanwhile, three-way catalytic converters are currently the most widely used exhaust gas post-treatment technology in motor vehicles; The principle is that the three-way catalytic converter is installed in the exhaust pipe after the exhaust manifold and before the exhaust muffler. When the engine is working, the exhaust gas enters the three-way catalytic converter through the exhaust pipe, converting harmful substances such as hydrocarbons, carbon monoxide, and nitrogen oxides in the car exhaust system into water vapor, carbon dioxide, and nitrogen.
| project | ||||
| Thermal shock resistance | Keep at 550 ºC for 30 minutes, quickly remove and cool at room temperature for 30 minutes. Repeat this process continuously for 3 times | muffle furnace | ||
| compressive strength | A-axis | >=7Mpa | Compression strength machine | |
| B-axis | >=2Mpa | |||
| Thermal expansion coefficient (room temperature -800 ºC) | ≤1.0*10 -6/ºC(A-axis) | Thermal expansion coefficient meter | ||
| Water absorption rate | 22%-26% | Electronic scale | ||
| Content of main crystal phase in cordierite | >=90% | XRD | ||
| verticality | Height ≤ 100 mm, verticality ≤ 1 mm; Height>100 | |||
| Parallelism | Diameter ≤ 100mm, tolerance ≤ 1mm; Diameter>100mm, tolerance ≤ 1% of product outer diameter dimension. | |||
| chemical composition | AL203 | (49.7±1.5)%, | ||
| Mg0 | (13.5±1.5)%; | |||
| Si02 | (35.4±1.5)%, | |||