Ni80Cr20
Aviation, Electronics, Industrial, Medical
JIS, GB, DIN, BS, ASTM, AISI
>98%
Alloy
Nickel Strip
Not Powder
white
0.01-3mm*0.3-600mm
Small Order Accepted
bright
soft,1/4hard,1/2hard,hard,T-hard
1.04-1.18 ohm mm2/m
TANKII
Waterproof Paper, Weave Bag, Wooden Case
DIN 17470
China
7506200000
Product Description
(ni80cr20/ni70cr30/ni60cr15/ni35cr20/ni20cr25/ ni30cr20) Nickel Chrome Resistance Heating Strip
1.FeCrAl wire strip includes:
OCr13Al4,OCr19Al3,OCr21Al4,OCr20Al5,OCr25Al5,OCr21Al6,OCr21Al6Nb,OCr27Al7Mo2.
2.Nickel chrome wire Strip Bar includes: Cr25Ni20,Cr20Ni35,Cr15Ni60,Cr20Ni80.
3.Copper Nickel wire Strip includes:
CuNi1,CuNi2,CuNi5,CuNi8,CuNi10,CuNi14,CuNi19,CuNi23,CuNi30,CuNi34,CuNi44.
4.Constantan wire includes: 6J40,4J42,4J32.
5.Manganin wire:6J8,6J12,6J13.
Deliveried surface conditions:
Bright annealed
Oxidized
Pickled
Enameled / PVC insulation
Main Property
Main advantage and application
It widely used in surtur and sulfide environment and producing industrial electric
furnace, household electrical appliance and far infrared ray device.
1.FeCrAl wire strip includes:
OCr13Al4,OCr19Al3,OCr21Al4,OCr20Al5,OCr25Al5,OCr21Al6,OCr21Al6Nb,OCr27Al7Mo2.
2.Nickel chrome wire Strip Bar includes: Cr25Ni20,Cr20Ni35,Cr15Ni60,Cr20Ni80.
3.Copper Nickel wire Strip includes:
CuNi1,CuNi2,CuNi5,CuNi8,CuNi10,CuNi14,CuNi19,CuNi23,CuNi30,CuNi34,CuNi44.
4.Constantan wire includes: 6J40,4J42,4J32.
5.Manganin wire:6J8,6J12,6J13.
Deliveried surface conditions:
Bright annealed
Oxidized
Pickled
Enameled / PVC insulation
| Alloy Nomenclature Performance | Cr20Ni80 | Cr30Ni70 | Cr15Ni60 | Cr20Ni35 | Cr20Ni30 | |
| Main Chemical | Ni | Rest | Rest | 55.0-61.0 | 34.0-37.0 | 30.0-34.0 |
| Cr | 20.0-23.0 | 28.0-31.0 | 15.0-18.0 | 18.0-21.0 | 18.0-21.0 | |
| Fe | ≤1.0 | ≤1.0 | Rest | Rest | Rest | |
| Max. continuous service temp. of element(ºC) | 1200 | 1250 | 1150 | 1100 | 1100 | |
| Resistivity at 20ºC (μΩ·m) | 1.09 | 1.18 | 1.12 | 1.0 | 1.04 | |
| Density(g/cm3) | 8.40 | 8.10 | 8.20 | 7.90 | 7.90 | |
| Thermal conductivity (KJ/m·h·ºC) | 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | |
| Coefficient of lines expansion(α×10-6/ºC) | 18.0 | 17.0 | 17.0 | 19.0 | 19.0 | |
| Melting point approx.( ºC) | 1400 | 1380 | 1390 | 1390 | 1390 | |
| Elongation at rupture(%) | >20 | >20 | >20 | >20 | >20 | |
| Micrographic structure | austenite | austenite | austenite | austenite | austenite | |
| Magnetic properties | nonmagnetic | nonmagnetic | Weak magnetic | Weak magnetic | Weak magnetic | |
Main Property
| Alloy material | Chemical composition % | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| max(≤) | |||||||||
| 1Cr13Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 12.5-15.0 | ---- | 3.5-4.5 | Rest |
| 0Cr15Al5 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 14.5-15.5 | ---- | 4.5-5.3 | Rest |
| 0Cr25Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 23.0-26.0 | ≤0.60 | 4.5-6.5 | Rest |
| 0Cr23Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | Rest |
| 0Cr21Al6 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 19.0-22.0 | ≤0.60 | 5.0-7.0 | Rest |
| 0Cr21Al4 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 21.0-23.0 | ≤0.60 | 3.0-5.2 | Rest |
| 0Cr21Al6Nb | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.60 | 21.0-23.0 | ≤0.60 | 5.0-7.0 | Rest |
| 0Cr27Al7Mo2 | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.40 | 26.5-27.8 | ≤0.60 | 6.0-7.0 | Rest |
Main advantage and application
It widely used in surtur and sulfide environment and producing industrial electric
furnace, household electrical appliance and far infrared ray device.