clear and matte Thermal Transfer PET film (Polyester Film) has good printability, excellent dimensional stability, good surface and barrier properties. clear thermal transfer PET film (polyester film) thickness is 16,18,19 micron, and matt thermal transfer PET film (polyester film regular thickness is 19 micron ,23 micron
PET film (Polyester Film) is used successfully in a wide range of applications, due to its excellent combination of optical, physical, mechanical, thermal, and chemical properties, as well as its unique versatility.
Characteristics:
1). Optically brilliant, clear appearance
2). Unequaled mechanical strength and toughness
3). Excellent dielectric properties
4). Good flatness and coefficient of friction (COF)
5). Tear-resistant and puncture-resistant characteristics
6). Excellent dimensional stability over a wide range of temperatures
7). Very good resistance to most common solvents, moisture, oil, and grease
8). Excellent barrier against a wide range of gases.
9). Widely use for packaging, printing, laminating, metallizing, decroation, electrical insulation.
PET film (Polyester Film) is used successfully in a wide range of applications, due to its excellent combination of optical, physical, mechanical, thermal, and chemical properties, as well as its unique versatility.
Characteristics:
1). Optically brilliant, clear appearance
2). Unequaled mechanical strength and toughness
3). Excellent dielectric properties
4). Good flatness and coefficient of friction (COF)
5). Tear-resistant and puncture-resistant characteristics
6). Excellent dimensional stability over a wide range of temperatures
7). Very good resistance to most common solvents, moisture, oil, and grease
8). Excellent barrier against a wide range of gases.
9). Widely use for packaging, printing, laminating, metallizing, decroation, electrical insulation.
| Properties | Units | Typical Values | Test Methods | |
| Tensile Strength | MD | MPa | ≥210 | ASTM D882 |
| TD | MPa | ≥210 | ||
| Elongation | MD | % | ≥90 | ASTM D882 |
| TD | % | ≥90 | ||
| Heat Shrinkage | MD | % | ≤2.0 | ASTM D1204 |
| TD | % | ≤1.0 | ||
| Wetting Tension ge | Dyne/cm | ≥52 | ASTM D2578 | |
| Co-efficient of Friction | Static TF/(TFC) | 0.55/0.60 | ASTM D1894 | |
| Dynamic TF/(TFC) | 0.50/0.55 | |||
| Haze | % | ≤3.0 | ASTM D1003 | |
| Light Transmission | % | ≥87 | ASTM D1003 | |
| Thickness | mic | 8 | PCL Method |
| Thickness Tolerance | % | +/- 3 | - |
| Width Tolerance | mm | +/- 2 | - |
| Lateral Edges Alignment | mm | ≤2 | - |
| Splice | Unit/roll | ≤1 | - |
| Splice Percent Per Shipment | % | ≤15 | - |