K10 tungsten carbide bar stock for tile mould in h
Without Logo Printing
Tungsten Carbide Strip/Flat Bars for Ceramic Mould
Customized
Cutting Tool
100% Raw Material Tungsten Carbide
ISO 9001:2008
K10
Ceramic Tile Moulds and Punch
>91.0 Hra
2800~3200 MPa
14.6~15.0
Ultrafine
High Hardness
Ceramic Tile Moulds and Punch
0~+2.0mm
0~+0.5mm
UBT
First in Paper Box, Then in Cartons or Wood Cases
5x25x335/345, 5x30x335/345mm
China
8209002900
Product Description
Tungsten carbide strip has high hardness and high wear resistance, it is a ideal choice to used in cutting kinds of wood.
With high quality raw material and advanced equipment, Zzbetter provides customer superior quality carbide strips.
- Easy to be brazed, good wear resistance and toughness.
- Untrafine grain size raw material to keep excellent strength and hardness.
- Both standard sizes and customizes sizes are available.
Grade Recommented:
| ZZBT Grade | ISO Grade | Density (g/cm3) | Hardness (HRA) | T.R.S (MPα) | Grain Size | Performance & Application Recommended |
| UBT910 | K20 | 14.6-15.0 | 90~90.5 | 2200~2400 | Medium | High hardness, suitable for roughing of iron, solid wood, dry wood or nonferrous metal, ceramic and other alloys. |
| UBT40S | K25 | 14.6-15.0 | 90~90.5 | 2600~2800 | Fine | High toughness, easy to be brazed without heat preservation. Suitable for rosewood, solid wood, pinewood, and other wood with a lot stammer. |
| UBT920 | K10~K15 | 14.6-15.0 | 91~91.8 | 2400~2600 | Fine | Good versatility, suitable for kinds of solid wood, rosewood, and MDF. |
| UBT15T | K10~K15 | 14.6-15.0 | 92.5~93 | 2000~2200 | Ultrafine | High hardness, suitable for finishing of iron, nonferrous metal, ceramic and other alloying, semifinishing of of hardwood, chipboard, MDF and HDF. Heat preservation is necessary when brazing. |
| UBT10T | K10 | 14.6-15.0 | 92.5~93 | 1800-2000 | Ultrafine | High hardness, suitable for finishing of iron, nonferrous metal, ceramic and other alloying, semifinishing of of hardwood, chipboard, MDF and HDF. Better to use silver soldering. |
| UBT10C | K40 | 13.8-14.2 | 87.5~88 | 2800~3000 | Coarse | High toughness, difficult to break tooth. Special used for finger jointing tool. |
Types and Sizes
| Type | T*W*L (mm) | T (mm) | W (mm) | L (mm) |
| FS05 | T x 5 x 320 | 2.0~15.0 | 5 | 320 |
| FS06 | T x 6 x 320 | 2.0~15.0 | 6 | 320 |
| FS07 | T x 7 x 320 | 2.0~15.0 | 7 | 320 |
| FS08 | T x 8 x 320 | 2.0~15.0 | 8 | 320 |
| FS09 | T x 9 x 320 | 2.0~15.0 | 9 | 320 |
| FS10 | T x 10 x 320 | 2.0~15.0 | 10 | 320 |
| FS11 | T x 11 x 320 | 2.0~15.0 | 11 | 320 |
| FS12 | T x 12 x 320 | 2.0~15.0 | 12 | 320 |
| FS13 | T x 13 x 320 | 2.0~15.0 | 13 | 320 |
| FS14 | T x 14 x 320 | 2.0~15.0 | 14 | 320 |
| FS15 | T x 15 x 320 | 2.0~15.0 | 15 | 320 |
| FS16 | T x 16 x 320 | 2.0~15.0 | 16 | 320 |
| FS17 | T x 17 x 320 | 2.0~15.0 | 17 | 320 |
| FS18 | T x 18 x 320 | 2.0~15.0 | 18 | 320 |
| FS19 | T x 19 x 320 | 2.0~15.0 | 19 | 320 |
| FS20 | T x 20 x 320 | 2.0~15.0 | 20 | 320 |
| FS22 | T x 22 x 320 | 2.0~15.0 | 22 | 320 |
| FS25 | T x 25 x 320 | 2.0~15.0 | 25 | 320 |
| FS28 | T x 28 x 320 | 2.0~15.0 | 28 | 320 |
| FS30 | T x 30 x 320 | 2.0~15.0 | 30 | 320 |
| FS32 | T x 32 x 320 | 2.0~15.0 | 32 | 320 |
| FS35 | T x 35 x 320 | 2.0~15.0 | 35 | 320 |
| FS40 | T x 40 x 320 | 2.0~15.0 | 40 | 320 |
| FS45 | T x 45 x 320 | 2.0~15.0 | 45 | 320 |
| FS50 | T x 50 x 320 | 2.0~15.0 | 50 | 320 |
| FS55 | T x 55 x 320 | 2.0~15.0 | 55 | 320 |
| Tolerance (mm) | ||
| L | >150 | -0~+L*2% |
| W | ≤8.0 | -0~+0.35 |
| 8.0~25.0 | -0~+0.50 | |
| 25.0~35.0 | -0~+0.70 | |
| >35.0 | -0~+1.20 | |
| T | ≤15.0 | -0~+0.40 |
| Flatness (mm) | ||
| W | ≤20.0 | ≤0.50 |
| >20.0 | ≤0.60 | |