1.Product Name:ISO 21988JNHBW555XCr27 High Wear Sand Cast Parts
2.Material Grade:HBW600 XCr20Mo2Cu
3.Hardness:More Than HRC56
4.Microstructure:Acicular Martensitic + Carbide + Residual Austenite < 6%
5.Certification:ISO9001-2018
6.Service:OEM,ODM
7.Chemical Composition:
Eqv. Standards | Nominal Chemical Composition (W%) | ||||||||
C | Si | Mn | Ni | Cr | Mo | Cu | P | S | |
EN-GJN-HV600(XCr11) ASTM A532 12% Cr | 1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 11.0-14.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
EN-GJN-HV600(XCr14) ASTM A532 15% Cr-Mo AS 2027 CrMo 15 3 G-X 300 CrMoNi 15 2 1 | 1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 14.0-18.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
EN-GJN-HV600(XCr18) ASTM A532 20% Cr-Mo AS 2027 CrMo 20 1 G-X 260 CrMoNi 20 2 1 | 1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 18.0-23.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
EN-GJN-HV600(XCr23) ASTM A532 25% Cr-Mo AS 2027 Cr27 LC & Cr27 HC G-X 260 Cr27 | 1.8-3.6 | ≤1.0 | 0.5-2.0 | ≤2.0 | 23.0-30.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 |
AS 2027 Cr35 | 3.0-5.5 | ≤1.0 | 1.0-3.0 | ≤1.0 | 30.0-40.0 | ≤1.5 | ≤1.2 | ≤0.06 | ≤0.06 |
AS 2027 CrMoCu 20 2 1 | 2.6-2.9 | ≤1.0 | ≤1.0 | ≤1.0 | 18.0-21.0 | 1.4-2.0 | 0.8-1.2 | ≤0.06 | ≤0.06 |
Q: Are you trading company or manufacturer ?
A: We are factory.
Q: How long is your delivery time?
A: Generally it is 5~10 days if the goods are in stock.Or it is 45 days if the goods are not in stock, it is according to quantity.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 50% T/T in advance ,balance before shipment
irrevocable LC at sight.