Product Description
ZIRCONIA FUSED MULLITE FZM33 FOR REFRACTORY
SHPAE IN BLOCK, 0-1MM, 1-3MM, 3-5MM
ENSURED QUALITY, COMPETITIVE PRICE
Fused zirconia mullite is a synthetic material manufactured with a high purity alumina oxide 98.5%min and first grade refined zircon ore ZrO2 65%min in high temperature melting in the electrical furnace. It has high purity and good crystal and excellent anti-corrosion properties.
Fused zirconia mullite is a ideal raw mateial for manufacture Al Zr-C slide plate fro continuous casting and long nozzle in metallurgical industry and for glass industry.
Fused zirconia mullite specification as follows:
SHPAE IN BLOCK, 0-1MM, 1-3MM, 3-5MM
ENSURED QUALITY, COMPETITIVE PRICE
Fused zirconia mullite is a synthetic material manufactured with a high purity alumina oxide 98.5%min and first grade refined zircon ore ZrO2 65%min in high temperature melting in the electrical furnace. It has high purity and good crystal and excellent anti-corrosion properties.
Fused zirconia mullite is a ideal raw mateial for manufacture Al Zr-C slide plate fro continuous casting and long nozzle in metallurgical industry and for glass industry.
Fused zirconia mullite specification as follows:
| Item | Chemical composition (%) | |||||||
| FZM 33 | ZrO2 ≥ | Al2O3 ≥ | SiO2 ≤ | Mullite content ≥ | Corundum content ≤ | glass phase ≤ | baddeleyite content ≥ | |
| 33 | 42 | 20 | 51 | 5 | 5 | 31 | ||
| Physical property | ||||||||
| color | bulk density g/cm3 ≥ | apparent porosity % ≤ | ||||||
| gray&yellow | 3.6 | 3 | ||||||