PVDF resin extrusion grade
24937-79-9
(CH2CF2)N
24937-79-9
REACH
Non-Pfoa
Heat Resistance
Powder
White
Indutrial Piping, Tanks, Valves, Fittings
6-26
165-170
74-80
FeiTengYa
Bag
PVDF
China
3904690000
Product Description
PVDF resin for molding, extrusion and architecture grade film.
It is a polyvinylidenefluoride polymer prepared by emulsion process, It has high melt viscosity and belongs to thermoplastic resin.
Its high purity, with excellent chemical corrosion resistance, oxidation resistance, radiation resistance and good mechanical properties, suitable for architecture grade film application and this resin is suitable to be molded into pipe fittings, pumps and valves and other parts of various specifications
It is a polyvinylidenefluoride polymer prepared by emulsion process, It has high melt viscosity and belongs to thermoplastic resin.
Its high purity, with excellent chemical corrosion resistance, oxidation resistance, radiation resistance and good mechanical properties, suitable for architecture grade film application and this resin is suitable to be molded into pipe fittings, pumps and valves and other parts of various specifications
| No. | Properties | Unit | Typical value | Test method |
| 1 | Appearance | - | White particle | Visual inspection |
| 2 | Solubility(DMAC) | - | Clear and transparent solution without impurities | T-FSI 027-2019 |
| 3 | Density | g/cm3 | 1.77-1.79 | GB/T 1033.1 |
| 4 | Water content | Wt% | ≤0.10 | HG/T 2902 |
| 5 | Durometer hardness | Shore D | 74~80 | ASTM D2240, GB/T 2411 |
| 6 | MFR@230ºC 5kg | g/10min | 6~26 | ASTM D1238 |
| 7 | Tensile breaking strength | Mpa | ≥25 | ASTM D638, GB/T1040.1 50mm/min@23ºC |
| 8 | Elongation at break | % | ≥20 | |
| 9 | Tensile Strength, Yield | Mpa | ≥25 | |
| 10 | Elongation at Yield | % | ≥10 | |
| 11 | Melting Point | ºC | 165~170 | GB/T 19466.4 |
| 12 | Thermal decomposition temperature | ºC | 370 | TGA |