Product Description
Refractory castable is a granulated and powdery material made by adding a certain amount of binder to refractory aggregate. It has high fluidity and is shaped by casting. The castable binder produced by our company has high moisture content, good fluidity, high strength and corrosion resistance, and can be selected according to the conditions of use. It can be directly poured into the lining body, and can be made into prefabricated blocks by pouring or shaking. It is mainly used for the lining parts of various industrial kilns such as incinerators and non-ferrous metal smelting furnaces.
Features Of Refractory CastableHigh refractoriness, High refractoriness under load
High density, low porosity
Good slag resistance and corrosion resistance
High strength and wear resistance
Good resistance to flake performance
Good thermal shock stability
Scouring resistance
Good hot strength
Applications Of Refractory Castable
mainly used in heat treatment furnace,heating furnace,soaking pit furnace,tundish slag dam weir,seconclary refining and the catalytic cracking unit etc key part of kiln furnace and thermal equipment.
Brand Properties | CA-190 | CA-185 | CA-180 | CA-175 | CA-170 | CA-165 | CA-160 | CA-155 | CA-150 | CA-140 | |
| Application Limit TempºC | 1,800 | 1,800 | 1,750 | 1,700 | 1,700 | 1,650 | 1,600 | 1,550 | 1,500 | 1,400 | |
| Bulk Density (g/cm3) | 2.90 | 2.85 | 2.80 | 2.60 | 2.50 | 2.30 | 2.15 | 2.10 | 2.10 | 2.00 | |
| Water Required for Casting (%) | 9-10 | 9-10 | 11-12 | 11-12 | 10-13 | 11-14 | 12-15 | 13-16 | 13-16 | 13-17 | |
| CCS/MOR (MPa) | 110ºCx24h | 55(9) | 30(6) | 30(6) | 30(6) | 25(5) | 25(5) | 20(4) | 20(4.5) | 25(5) | 20(5) |
| 1,200ºCx3h | 50(8) | 35(7) | 35(7) | 30(7) | 20(4) | 17(3.5) | 15(3.5) | 15(2.5) | 17(4) | 14(3) | |
| 1,400ºCx3h | 60(10) | 50(8) | 60(10) | 60(10) | 50(12) | 45(8) | 40(7) | 40(7) | 32(7.5) | - | |
| Permanent Linear Change (%) | 110ºCx24h | -0.03 | -0.03 | -0.06 | -0.06 | -0.06 | -0.06 | -0.06 | -0.06 | -0.06 | -0.06 |
| 1,200ºCx3h | -0.10 | -0.10 | -0.15 | -0.15 | -0.20 | -0.20 | -0.16 | -0.30 | -0.25 | -0.30 | |
| 1,400ºCx3h | -0.20 | -0.20 | -1.0 | -1.0 | -0.8 | -1.0 | -1.0 | -0.7 | - | - | |
| (W/m.k) Thermal conductivity | 400ºC | 0.95 | 0.95 | 0.92 | 0.92 | 0.80 | 0.72 | 0.68 | 0.68 | 0.65 | 0.60 |
| 1,000ºC | 1.1 | 1.05 | 1.02 | 1.02 | 0.90 | 0.85 | 0.88 | 0.80 | 0.76 | 0.71 | |
| (%) Chemical Analysis | Al2O3 | 92 | 88 | 82 | 75 | 62 | 55 | 50 | 47 | 44 | 35 |
| SiO2 | - | - | 10 | 10 | 29 | 40 | 43 | 45 | 50 | 55 | |