Product Description
910HT
Direct Roving-------- Designed for Winding/ Pultrusion/ Weaving Process
Product Description
910HT is an E-glass or TCR (ECR) single-end continuous roving without mechanical twist. TCR is a boron-free, fluorine-free and environmentally friendly glass, with excellent acid resistance.
Designed for winding, pultrusion and weaving process, 910HT is a general purpose product, typically used to produce FRP products, such as pipes, tanks, molded GRP grids and pultruded products. It can also be used to manufacture woven roving.
Silane-based sizing, compatible with Unsaturated Polyester (UP), Vinyl Ester (VE), Epoxy (EP) and Polyurethane (PU) resin systems.
Characteristics Product Code
Even Tension and High Strand Integrity TCR 910HT - 2400 - 24
Superior Processing Properties and Less Fuzz TCR E-glass Chemical Resistant
Consistent Linear Density and High Filament Strength 910HT Sizing Code
Fast Wet-out and Good Ultimate State 2400 2400tex
Excellent Composite Properties 24 Filament Diameter
Technical Data
Specification
Note: Tex can be adjusted to the requirement of customers.
Composite Performance
Note: Use UP resin.
Note: Use EP resin with anhydride curing agent as matrix.
Packaging
Each roll (14-22kg) is wrapped in PE film, stacked on pallets or put into cartons. Each pallet stacks 36, 48 or 64 rolls. All pallets should be stacked ≤ 2 layers and Cartons ≤ 5 layers. Manner of packing can be customized.
Storage
This product should be stored in a dry, ventilated and rainproof place, with temperature from 5ºC to 35ºC and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.
Direct Roving-------- Designed for Winding/ Pultrusion/ Weaving Process
Product Description
910HT is an E-glass or TCR (ECR) single-end continuous roving without mechanical twist. TCR is a boron-free, fluorine-free and environmentally friendly glass, with excellent acid resistance.
Designed for winding, pultrusion and weaving process, 910HT is a general purpose product, typically used to produce FRP products, such as pipes, tanks, molded GRP grids and pultruded products. It can also be used to manufacture woven roving.
Silane-based sizing, compatible with Unsaturated Polyester (UP), Vinyl Ester (VE), Epoxy (EP) and Polyurethane (PU) resin systems.
Characteristics Product Code
Even Tension and High Strand Integrity TCR 910HT - 2400 - 24
Superior Processing Properties and Less Fuzz TCR E-glass Chemical Resistant
Consistent Linear Density and High Filament Strength 910HT Sizing Code
Fast Wet-out and Good Ultimate State 2400 2400tex
Excellent Composite Properties 24 Filament Diameter
Technical Data
| Moisture Content (%) | Loss on Ignition (%) | Linear Density (tex) (g/km) | Breaking Strength (N/Tex) |
| ≤0.10 | 0.55±0.15 | Tex±5% | ≥0.40 |
| Tex |
| 275, 300 ,400, 410, 600, 735, 900, 1100, 1200,1500, 1700, 1800, 2000, 2200, 4400, 8800 ,9600 |
Composite Performance
| Property | Tensile Strength (Mpa) | Tensile Modulus (Gpa) | Shear Strength (Mpa) |
| Test Standard | ASTM D2343 | ASTM D2343 | ASTM D2344 |
| Test Value | 2668 | 82.50 | 58.55 |
| Property | Tensile Strength (Mpa) | Tensile Modulus (Gpa) | Shear Strength (Mpa) |
| Test Standard | ASTM D2343 | ASTM D2343 | ASTM D2344 |
| Test Value | 2530 | 82.32 | 65.25 |
Packaging
Each roll (14-22kg) is wrapped in PE film, stacked on pallets or put into cartons. Each pallet stacks 36, 48 or 64 rolls. All pallets should be stacked ≤ 2 layers and Cartons ≤ 5 layers. Manner of packing can be customized.
| Layer | 3 | 4 | 3 | 4 |
| Rolls/Layer | 16 | 12 | ||
| Rolls/Pallet | 48 | 64 | 36 | 48 |
| Pallet Dimensions (mm) | 1120*1120*135 | 1280*960*130 | ||
| Net Weight/Pallet (kg) | 816 | 1088 | 792 | 1056 |
Storage
This product should be stored in a dry, ventilated and rainproof place, with temperature from 5ºC to 35ºC and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.