FT1100 steel strip is made of hardened carbon steel. Its smooth, hard surface with a black oxide layer is suitable for any application with a low risk of corrosion, and its excellent thermal conductivity makes it ideal for baking as well as heating and drying liquid, pasty and fine-grained products.
Tensile strength:1100 Mpa
Yield strength:960 Mpa
Fatigue Strength:460 Mpa
Hardness:35±1 HRC
Elongation:5%
Weld factor:0.75
Product DescriptionFT1100 steel strip is made of hardened carbon steel. Its smooth, hard surface with a black oxide layer is suitable for any application with a low risk of corrosion, and its excellent thermal conductivity makes it ideal for baking as well as heating and drying liquid, pasty and fine-grained products.
Chemical Composition (Nominal)%C
Si
Mn
P
S
Cr
Cu
Ni
Al
Fe
0.65
0.24
1.00
<0.03
0.002
0.22
0.02
0.01
0.022
-
Static Strength
Standard strength at room temperature (nominal values)
Parametric
Tensile strength
Yield strength
Elongation
Weld factor
Hardness
Mpa
Mpa
A5(%)
Rm/Rm
HRC
Base material
1100
960
8
·
35±1
Welding area
800
650
5
0.75
·
Scope of supplyLength Customizable
Width 600/800/1000/1200/1500/…mm
Thickness 0.8/1.2/1.4/1.5mm
Note The Rebo steel strip comes in a width of 1500mm, but can be customized to different sizes through cutting or longitudinal welding.