Hastelloy C-4
Aviation, Electronics, Industrial, Medical, Chemical
JIS, GB, DIN, BS, ASTM, AISI
Alloy
Nickel Bar
Not Powder
Mingson
Wooden Crate
As customers's request
China
7505120000
Product Description
Alloy C-4 has outstanding high-temperature stability, and has excellent resistance to stress-corrosion cracking and oxidizing atmospheres up to 1040ºC. It has exceptional resistance to a wide variety of chemical process environments, including hot contaminated mineral acids, solvents, chlorine and chlorine contaminated media (organic and inorganic), formic and acetic acids, acetic anhydride, and
seawater and brine solutions.
CHEMICAL COMPOSITION
THE MINIMUM MECHANICAL PROPERTIES AT NORMAL TEMPERATURE
CHEMICAL COMPOSITION
| C | Mn | Fe | P | S | Si | Cu | Ni | Co | Al | Ti | Cr | Nb+Ta | Mo | B | N | W | La | V | Nb | |
| Hastelloy B | ≤0.05 | ≤1.0 | 4.0-6.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | ≤1.0 | 26.0-30.0 | 0.2-0.4 | |||||||||
| Hastelloy B-2 | ≤0.01 | ≤1.0 | ≤2.0 | ≤0.02 | ≤0.03 | ≤0.01 | balance | ≤1.0 | 0.04-0.07 | 26.0-30.0 | ||||||||||
| Hastelloy C | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | 50.0-58.0 | 14.5-16.5 | 15.0-17.0 | |||||||||||
| Hastelloy C-4 | ≤0.015 | ≤1.0 | ≤3.0 | ≤0.04 | ≤0.03 | ≤0.08 | balance | ≤2.0 | ≤0.7 | 14.0-18.0 | 14.0-17.0 | |||||||||
| Hastelloy C-22 | ≤0.015 | ≤0.5 | 2.0-6.0 | ≤0.02 | ≤0.35 | ≤0.08 | balance | ≤2.5 | 20.0-22.5 | 12.5-14.5 | 2.5-3.5 | 0.02 | ||||||||
| Hastelloy C-276 | ≤0.08 | ≤1.0 | 4.0-7.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | ≤2.5 | 14.5-16.5 | 15.0-17.0 | 3.0-4.5 | ≤0.35 | ||||||||
| Hastelloy C-2000 | ≤0.01 | ≤0.5 | ≤3.0 | ≤0.025 | ≤0.01 | ≤0.08 | 1.3-1.9 | balance | ≤2.0 | ≤0.5 | 22.0-24.0 | 15.0-17.0 | ||||||||
| Hastelloy G-30 | ≤0.03 | 0.3-1.5 | 13.0-17.0 | ≤0.04 | ≤0.02 | 0.2-0.8 | 1.0-2.4 | balance | ≤5.0 | 28.0-31.5 | 4.0-6.0 | 1.5-4.0 | 0.3-1.5 | |||||||
| Hastelloy G-35 | ≤0.05 | ≤0.5 | ≤2.0 | ≤0.03 | ≤0.015 | ≤0.6 | ≤0.30 | balance | ≤1.0 | ≤0.4 | 32.25-34.25 | 7.6-9.0 | ≤0.6 | ≤0.2 | ||||||
| Hastelloy X | 0.05-0.15 | ≤1.0 | 17.0-20.0 | ≤0.04 | ≤0.03 | ≤1.0 | balance | 0.5-2.5 | 20.5-23.0 | 8.0-10.0 | 0.2-1.0 | |||||||||
| Hastelloy S | ≤0.02 | 0.3-1.0 | ≤3.0 | ≤0.02 | ≤0.015 | 0.2-0.75 | balance | ≤2.0 | 0.1-0.5 | 14.5-17.0 | 14.0-16.5 | ≤1.0 | 0.01-0.1 |
THE MINIMUM MECHANICAL PROPERTIES AT NORMAL TEMPERATURE
| Alloy and State | Tensile Strength | Yield Strength | Rate of Elongation | Brinell Hardness |
| Rm N/mm2 | RP0.2N/mm2 | A5% | HB | |
| Hastelloy B | ≥760 | ≥350 | ≥40 | - |
| Hastelloy B-2 | ≥760 | ≥350 | ≥40 | - |
| Hastelloy C | 690 | 310 | 40 | - |
| Hastelloy C-4 | ≥690 | ≥276 | ≥40 | - |
| Hastelloy C-22 | ≥690 | ≥310 | ≥45 | - |
| Hastelloy C-276 | ≥690 | ≥283 | ≥40 | - |
| Hastelloy C-2000 | ≥690 | ≥283 | ≥45 | - |
| Hastelloy G-30 | ≥586 | ≥241 | ≥30 | - |
| Hastelloy X | ≥586 | ≥241 | ≥30 | - |
| Hastelloy S | ≥110 | ≥52 | ≥46 | - |