LT-PGW
Automotive Wiring, Electrical Insulation, HVAC System, Pipe Insulation
White
Glass Fiber
20KV~100KV
H 180
10mm, 15mm, 20mm, 25mm, 30mm, 32mm, 35mm, 40mm
0.17mm, 0.2mm, 0.25mm, 0.3mm, 0.32mm
Fiber Glass Yarn + Unsaturated Polyester Rein
50~200 Meters Per Roll
F, H Grade
Solid
Inorganic Insulation
Inorganic Insulation Material
ISO9001
Lontom
LONTOM
Spool
RoHS
Shanghai, China
70199000
Product Description
Electric Insulating Edge Banding Tape
1.Thickness:0.2~0.5mm
2.Fiberglass banding tape
3.Self-adhesive insulation tape
4.SGS,RoHS
The banding tapes are of high quality, which consist of parallel twisted E-glass yarns preimpregnated with a special thermosetting polyester resin and manufactured with the proprietory technology and advanced equipments.
It's widely used in AC. DC motors, generators and transformers especially in traction motors.
Main Properties:
1.Thickness: 0.20mm±10%,0.30mm±10%
2.Width: 10mm~50mm±10%
3.Length/Spool: 50~200 meters
4.Standard color: White
5.Thermal Grade: F grade(155ºC)
H grade(180ºC)
6.Curing condition (Time to bring the piece to the temperature is not considered)
| Temperature | ºC | 160 | 150 | 135 | 120 | 115 |
| Time | hour | 2.5 | 3 | 5 | 14 | 20 |
7.Storage Stability:
| Storage temperature | ºC | 10 | 15 | 20 | 30 |
| Time | Month | 20 | 15 | 10 | 6 |
Technical Data:
| Test content | Unit | Standard Value | ||
| Thermal class | H | F | ||
| Volatile content | % | ≤ 2 | ||
| Loss of weight at calcination | % | 26±2 | ||
| Soluble resin content | % | ≥ 90 | ||
| Tensile strength before curing | N/cm | ≥1500 | ≥1000 | |
| Maximum pull while banding | N/cm | 800 | 800 | |
| Tensile strength of ringlike sample at room temperature after curing | Mpa | 20ºC | ||
| above :900 | above :900 | |||
| Tensile strength of ringlike sample at working temperature after curing | Mpa | 180ºC | 150ºC | |
| ≥600 | ≥560 | |||
| Proof tracking index | ≥500V | |||
| Arc resistance | S | ≥160 | ||
| Breakdown voltage parallel to layers | KV | normal condition:≥25 after soaked in water for 24 hours:≥10 | ||
| Thermosetting | OK | |||
| Loss of tensile strength after soaked in oil | ≤10% | |||
Package: