Ecofriendly flame retardent masterbatch for polypropylene, 2% dosage to pass UL94-V2
Introduction
Mflam MB AMH-01S is a flame retardant especially designed for polyolefin, with phosphorus, bromine and nitrogen as the main flame retardant elements. It has high flame retardant efficiency, add 2%-3% in homo poly PP (add 5%-6% in co-polymer PP ), to achieve UL94 V2. Good thermal stability, no immigration, excellent water resistance, good aging resistance and low smoke non-toxicity, no heavy metal, will not influence the transparent color of PP.
Specification:
Package Information:
25Kg paper bag, 1*20' fcl=17.5mt with pallets.
Recommended dosage:
Remarks:
Introduction
Mflam MB AMH-01S is a flame retardant especially designed for polyolefin, with phosphorus, bromine and nitrogen as the main flame retardant elements. It has high flame retardant efficiency, add 2%-3% in homo poly PP (add 5%-6% in co-polymer PP ), to achieve UL94 V2. Good thermal stability, no immigration, excellent water resistance, good aging resistance and low smoke non-toxicity, no heavy metal, will not influence the transparent color of PP.
Specification:
| Item | Index |
| Appearance | White granule |
| FR content % | 40 |
| PP Carrier % | 60 |
| Density g/cm3 | 1.0-1.2 |
| Process condition ºC | ≤180 |
Package Information:
25Kg paper bag, 1*20' fcl=17.5mt with pallets.
Recommended dosage:
| Resin | Homo poly PP | Copoly PP | Homo PP+20% talcum powder | Copoly PP+20% talcum powder |
| Dosage % Mflam MB AMH-01S | 2-3 | 5-6 | ≥3 | ≥7.5 |
| UL94 | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) | V-2(3.2mm) V-2(1.6mm) V-2(0.8mm) |
Remarks:
- The process temperature of Mflam MB AMH-01S is recommended under 230 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
- When add Mflam MB AMH-01S in PP, it is not suggested to use Strong shear screw combination.