Product Description
Copper Alloy CCA Cooper Clad Aluminium Wire
Application:
1.Lan Cable 2.Power Cable 3.Control Cable
4.Conductor for coaxial cables 5.Construction wiring 6.Bus-bar
7.Fuse 8.RF shielded cable 9.Extension-cord
Advantage:
1.Better price-less expensive than copper,reducing costs of material for cable production.
2.Higher conductivity-electrical conductivity much higher than pure aluminum.
3.Lighter weight-easy to transport and install thus saves labor cost.
| CCA Wire (AWG)Note: | Note: | ||||
| Technical Characteristics | Clad type | ||||
| 10H | 10A | 15H | 15A | ||
| Size range | 0.12mm-8.00mm | 0.12mm-8.00mm | 0.12mm-8.00mm | 0.12mm-8.00mm | |
| Copper content (by weight) | 25%-31% | 25%-31% | 32%-40% | 32%-40% | |
| Resistivity (max at 20ºC) | 0.02743 Ω.mm²/m | 0.02743 Ω.mm²/m | 0.02676 Ω.mm²/m | 0.02676 Ω.mm²/m | |
| Density | 3.32g/cm² | 3.32g/cm² | 3.63g/cm² | 3.63g/cm² | |
| Conductivity (max at 20ºC) | 62% | 62% | 64% | 64% | |
| Elongation | 1%-3% | 8%-25% | 1%-3% | 8%-25% | |
| Tensile Strength | ≥250Mpa | ≥110Mpa | ≥250Mpa | ≥110Mpa | |
Packaging Details:
| NO. | DIN130MM | DIN185MM | DIN250MM | DIN400MM | DIN800MM |
| A | 130MM | 185MM | 250MM | 400MM | 800MM |
| B | 65MM | 130MM | 160MM | 160MM | 370MM |
| C | 100MM | 160MM | 160MM | 260MM | 490MM |
| D | 120MM | 180MM | 200MM | 290MM | 520MM |
| E | 21MM | 31MM | 31MM | 56MM | 126MM |