SB-WRSFM
Insulators, Electrical Winding Insulation, Winding Wire Coating Insulation, Electrical Base, Shell, Motor, Insulating Varnish, Switch Baseplate
Black
Polyolefin
<10KV
E 120
-45~+105 C
110~130c
2:1
Black
6~240mm
22~270mm
Insulation Sleeve & Tube
Hybrid Insulation
Hybrid Insulation Materials
ISO9001, Iatf 16949
Sunbow
SUNBOW
Carton Package or Pallet Package
ID11~250MM
Shenzhen, China
3917310000
Product Description
Cable End Sealing Heat Shrink End Caps
Model Number: SB-WRSFM
Features
2:1 shrink ratio
Superior resistance to weathering
Resistant to common fluids
Standard adhesive liner provides coated hot melt adhesive resists continuous operating temperature
Shrink temperature: start at 110ºC, and fully recovered at 130ºC
Dimension
Technical Data
Model Number: SB-WRSFM
Features
2:1 shrink ratio
Superior resistance to weathering
Resistant to common fluids
Standard adhesive liner provides coated hot melt adhesive resists continuous operating temperature
Shrink temperature: start at 110ºC, and fully recovered at 130ºC
Dimension
| Size | Size after recovery(mm) | Size as supplied (mm) | Cable sizes(mm) | |||
| Inner Diameter | Wall thickness | Inner Diameter | Wall thickness | length | Outer Diameter | |
| Φ 11 | ≤6.5 | 1.1±0.1 | ≥11 | 0.7±0.2 | ≥22 | Φ6-9 |
| Φ 16 | ≤8.0 | 2.5±0.1 | ≥16 | 1.2±0.2 | ≥70 | Φ9-14 |
| Φ 20 | ≤8.0 | 2.5±0.1 | ≥20 | 1.2±0.2 | ≥70 | Φ9-17 |
| Φ 25 | ≤11 | 2.5±0.1 | ≥25 | 1.2±0.2 | ≥80 | Φ12-22 |
| Φ 32 | ≤17 | 2.6±0.1 | ≥32 | 1.5±0.2 | ≥90 | Φ17-27 |
| Φ 40 | ≤15 | 2.8±0.1 | ≥40 | 1.5±0.2 | ≥90 | Φ20-35 |
| Φ 55 | ≤25 | 2.8±0.1 | ≥55 | 1.5±0.2 | ≥125 | Φ28-45 |
| Φ 75 | ≤30 | 3.2±0.1 | ≥75 | 1.8±0.2 | ≥145 | Φ40-65 |
| Φ 100 | ≤42 | 3.5±0.1 | ≥100 | 1.8±0.2 | ≥140 | Φ50-90 |
| Φ 120 | ≤59 | 3.5±0.1 | ≥120 | 1.8±0.2 | ≥155 | Φ70-110 |
| Φ 140 | ≤63 | 4.0±0.1 | ≥140 | 2.0±0.2 | ≥180 | Φ90-130 |
| Φ 250 | ≤94 | 4.0±0.1 | ≥250 | 2.0±0.2 | ≥270 | Φ120-240 |
Technical Data
| Property | Test Method | Standard Value |
| Operating temperature | IEC 216 | -45ºC to+105ºC |
| Tensile strength | ASTM-D 2671 | ≥13MPa |
| Elongation at break | ASTM-D 2671 | ≥300% |
| Tensile strength after aging | ASTM-D-2671/120ºC,168hrs | ≥10MPa |
| Elongation at break after aging | ASTM-D-2671/120ºC,168hrs | ≥240% |
| Dielectric strength | IEC 243 | ≥15kV/mm |
| Volume resistance | ASTM-D-2303 | ≥1×1013Ohm.cm |
| Dielectric constant | IEC 250 | 3.0 |
| Radial shrinkage | - | ≥50% |
| Eccentricity | ASTM-D-2671 | ≤35% |
| Low Temperature Flexibility | ASTM-D-2671 | -40ºC, 4hrs, no cracking |
| Minimum shrink temperature | - | 90ºC |
| Minimum fully recovered temperature | - | 130ºC |