EP100~EP400, NN100~NN400 etc
Conveyor Belt
Heat-resistant, Tear-resistant, Flame-resistant
Materials Handling
Strong Rubber Conveyor Belt
Black
300~2000mm
3~30mm
8~25 MPa
JIUZHOU
Standard Packing
GB, DIN, RMA, ISO, AS, SABS, BS
Baoding City, Hebei, China
40101200
Product Description
Specification:
1) Carcass: EP100~EP400, NN100~NN400, TN/C & CC
2) No.s of ply: 2~10
3) Constructure: Fabric carcass, steel mesh reinforcement layer, top & bottom rubber cover
4) Delivery Detail: 20~30 working day for general orders
Characteristics:
1) Carcass: EP100~EP400, NN100~NN400, TN/C & CC
2) No.s of ply: 2~10
3) Constructure: Fabric carcass, steel mesh reinforcement layer, top & bottom rubber cover
4) Delivery Detail: 20~30 working day for general orders
Characteristics:
Belt body light and thin, high tensile strength, moisture resistant, fatigue resistant, impact resistant, excellent trough ability etc.
Classify by performance:
1) General use conveyor belt,
2) Oil-resistant conveyor belt,
3) Acid/alkali conveyor belt,
4) Cold-resistant conveyor belt,
5) Anti-static electricity conveyor belt, etc.
Application:
Widely used in coal mine and other fire or high-temperature occasions. | Specification | SN400 | SN630 | SN800 | SN1000 | SN1125 | |
| Tensile Strength (N/mm) | 400 | 630 | 800 | 1000 | 1125 | |
| Metal Mesh Thickness (mm) | 5.5 | 5.5 | 7.0 | 8.0 | 9.0 | |
| Top Rubber Cover Thickness (mm) | 6 | 8 | 9 | 10 | 10 | |
| Bottom Rubber Cover Thickness (mm) | 3 | 3 | 3 | 3 | 3 | |
| Interlayer Adhesive Strength Longitudinal Average Value of the Samples | Ordinary Temperuture | ≥10N/mm | ||||
| 160ºC | ≥4.0N/mm | |||||
| Min. Pulley Diameter (mm) | 150 | 200 | 300 | 400 | 500 | |
| Belt Width (mm) | 300-800 | |||||
| Cover Layer Physical Properties After Thermal Aging Test | |||||
| Item | Type | ||||
| Type1 | Type2 | Type3 | Type4 | ||
| Changing scope | |||||
| Hardness | Differences of before and after aging test | +20 | ±20 | ±20 | ±20 |
| Max. after aging test | 85 | 85 | 85 | 85 | |
| Tensile strength | Properties changing rate reducing | -25 | -30 | -40 | -40 |
| Min. after aging test | 12 | 10 | 5 | ||
| Elongation at breaking | Changing rate of properties | -50 | -50 | -55 | -55 |
| Min. after aging test | 200 | 200 | 180 | 180 | |
| Note: Aging test (100°Cx168h, 125°Cx168h, 150°Cx168h) | |||||