6150
ASTM
Ferrous Steel Scrap
Forged
Round, Square, Flat
Black, Grinded, Peeled, Polished, Rough Turned
Mold Steel
Structural Steel Bar
50CRV4, DIN 1.8519, BS970, En 47.
Diameter: 20-480mm
Annealed, Qunched and Tempered
Black, Grinded, Peeled, Polished
FUSHUN
Apply The Shipping Packing
Diameter: 20-480mm
Hubei, Huangshi
7228600000
Product Description
Similar Grades:
DIN1.8519, 50CrV4,BS970,EN47
Shape:
Round, Flat, Square.
Size Range:
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
Chemical Composition:
Heat Treatment:
Forging: Preheat carefully, then raise temperature to 1050°C for forging. Do not forge below 840°C. After forging cool slowly in a furnace.
Annealing: Heat slowly to 820-840°C, soak well and cool slowly in a furnace.
Hardening: Heat slowly to 650-700°C and thoroughly soak. Continue to heat the 6150 steel to the final hardening temperature of 830-860°C and allow to be heated through. Oil quench.
Tempering: Temper 6150 spring steel immediately after hardening whilst tools are still hand warm. Re-heat to the tempering temperature then soak for one hour per 25 millimetre of total thickness (2 hours minimum) Cool in air. Tempering of this grade will be between 400-600°C for most applications.
Introduction:
The 6150 Spring Steels receive their special characteristics through quenching and tempering.
The processors need to make sure that their calculation method, design technique and processing procedure are aligned with the material. Precise temperature control is crucial for the part's characteristics.
Therefore, the temperature needs to be adjusted according to the respective purpose of the material.
Applications:
Used widely in the motor vehicle industry AISI 6150 spring steels is suitable for many general engineering applications that require high tensile strength and toughness. Typical applications include crankshafts, steering knuckles, spindles, pumps and gears.
Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
Website: fushunmetal.en.made-in-china.com
DIN1.8519, 50CrV4,BS970,EN47
Shape:
Round, Flat, Square.
Size Range:
| Diameter(mm) | Thickness (mm) | Width (mm) | Length(mm) | |
| Round | 20-480 | - | - | 2000-5800 |
| Square | 20-480 | - | - | 2000-5800 |
| flat | - | 20-50 | 80-600 | 2000-5800 |
Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered
Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
| Packing details | In seaworthy packing, as your requirement. |
| Delivery details | within 30-50 days |
Chemical Composition:
C | Mn | P | S | Si | Cr | V |
| 0.48-0.53 | 0.70-0.90 | 0.035max | 0.040max | 0.15-0.35 | 0.90-1.10 | 0.15min |
Heat Treatment:
Forging: Preheat carefully, then raise temperature to 1050°C for forging. Do not forge below 840°C. After forging cool slowly in a furnace.
Annealing: Heat slowly to 820-840°C, soak well and cool slowly in a furnace.
Hardening: Heat slowly to 650-700°C and thoroughly soak. Continue to heat the 6150 steel to the final hardening temperature of 830-860°C and allow to be heated through. Oil quench.
Tempering: Temper 6150 spring steel immediately after hardening whilst tools are still hand warm. Re-heat to the tempering temperature then soak for one hour per 25 millimetre of total thickness (2 hours minimum) Cool in air. Tempering of this grade will be between 400-600°C for most applications.
Introduction:
The 6150 Spring Steels receive their special characteristics through quenching and tempering.
The processors need to make sure that their calculation method, design technique and processing procedure are aligned with the material. Precise temperature control is crucial for the part's characteristics.
Therefore, the temperature needs to be adjusted according to the respective purpose of the material.
Applications:
Used widely in the motor vehicle industry AISI 6150 spring steels is suitable for many general engineering applications that require high tensile strength and toughness. Typical applications include crankshafts, steering knuckles, spindles, pumps and gears.
Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
Website: fushunmetal.en.made-in-china.com