XGHSR-600S
Fiberglass Cloth
High Silica Glass
7micron
Fabric
High Silica Fiber
Xghsr-600s
White
Satin
100cm
50m
0.65mm
600G/M2
69X79PCS/5cm
620/500n/25X100mm
<7%
XIANGU
Cartons
108*28*28cm
China
7019909990
Product Description
600g High Silica Fiber Fabric is made of high silica fiberglass yarn,a kind of high-temperature inorganic fiber cloth coated with polyurethane,SiO2 is more than 94%,loss on ignition is less than 10%,has excellent chemical stability,good dielectric properties,thermal shock resistance,smooth surface,easy processing,used for strengthening and anti-ablation materials,producing anti-ablative products.Widely used in rockets,missiles, spacecraft thermal ablation materials,high temperature insulation,insulation materials.etc
SPECIFICATIONS:
ADVANTAGES:
1, softening point close to 1700 ºC,long-term use in the 900 ºC environment,it can work 10 minutes at 1450ºC and 15 seconds at 1600ºC, instantly can withstand thousands of degrees of air flow brush.
2, in organic and inorganic acids (hydrofluoric acid,phosphoric acid and hydrochloric acid excluded) even at high temperatures,weak alkaline solution to maintain good performance and stability.
3,meeting the thermal shock and high radiation,it has a high stability,excellent insulation properties in high temperature and high humidity conditions and good adhesion properties with high temperature adhesive.
4,resistance of moisture,Sunlight radiation and seismic,can be used for a variety of sealing materials,solid structure,in many high-temperature conditions to maintain flexibility.
5,the structure and performance stability,no harm to the human body,can replace the ceramic fiber and asbestos fibers (high temperature crystalline phase change occurred).
6,anti-high temperature fire,burning in the gasoline without oxidization,no color changing,high strength,no secondary pollution.
7,with good wear resistance and insulation properties.
STORAGE:
The product should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.
PACKAGING:
PRODUCT DETAIL IMAGES:
SPECIFICATIONS:
| Model: | XGHSR-600S |
| Color: | white |
| Weave: | Satin 8h |
| PU: | No |
| Width(cm): | 100±1 |
| Roll length(m); | 50 |
| Cloth thickness(mm): | 0.65±0.08 |
| GSM(g/m2): | 600±25 |
| Thread Count(pcs/5cm): | 69x 79 Length & Width |
| Strength at break(N/(25×100mm)): | Warp:620/Weft:500 |
| SiO2(%): | >94 |
| LOI(%): | <10.0 |
| Shrinkage(%): | ≤7 |
ADVANTAGES:
1, softening point close to 1700 ºC,long-term use in the 900 ºC environment,it can work 10 minutes at 1450ºC and 15 seconds at 1600ºC, instantly can withstand thousands of degrees of air flow brush.
2, in organic and inorganic acids (hydrofluoric acid,phosphoric acid and hydrochloric acid excluded) even at high temperatures,weak alkaline solution to maintain good performance and stability.
3,meeting the thermal shock and high radiation,it has a high stability,excellent insulation properties in high temperature and high humidity conditions and good adhesion properties with high temperature adhesive.
4,resistance of moisture,Sunlight radiation and seismic,can be used for a variety of sealing materials,solid structure,in many high-temperature conditions to maintain flexibility.
5,the structure and performance stability,no harm to the human body,can replace the ceramic fiber and asbestos fibers (high temperature crystalline phase change occurred).
6,anti-high temperature fire,burning in the gasoline without oxidization,no color changing,high strength,no secondary pollution.
7,with good wear resistance and insulation properties.
STORAGE:
The product should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire.
PACKAGING:
PRODUCT DETAIL IMAGES: