1430 Ceramic Fiber Vacuum Form Shape
1430ºC
Al2O3.SiO2
Ceramic Fiber Shape
Vacuum Wet Form
High Purity Ceramic Fiber
THERMOST
Wooden Box
According to Drawings
Shanghai China
6806101000
Product Description
Ceramic Fiber Vacuum Form Shape
Ceramic fiber vacuum form shape is made from made of ceramic fiber bulk as raw material, use metal mould and vacuum forming process. Complex and special shape can be customized.
Available type as following:
† R-Regular Type ( dry / organic)
† SH-Surface harden Type (dry / add surface strength / organic)
† EH-Entirety harden Type (dry / add entirety strength / organic)
† PF-Pre-fire Type( without smoke / low shrinkage/ inorganic)
† PFSH-Pre-fire Type and surface harden (without smoke / add surface strength / low shrinkage/inorganic)
1430 Ceramic Fiber Vacuum Form Shapes (RCF)
WITH ZIRCONIA
1430 Shape made from ceramic fiber bulk (Al2O3+SiO2+ZrO2), It is produced by wet vacuum forming process. After drying, finish grinding, cutting and other finishing processes to ensure the shape's precision. It has excellent mechanical properties and wind corrosion resistance, and can be directly used for thermal insulation on the hot surface and high temperature equipment.
Recommended max continuous use ≤1250ºC
Ceramic fiber vacuum form shape is made from made of ceramic fiber bulk as raw material, use metal mould and vacuum forming process. Complex and special shape can be customized.
Available type as following:
† R-Regular Type ( dry / organic)
† SH-Surface harden Type (dry / add surface strength / organic)
† EH-Entirety harden Type (dry / add entirety strength / organic)
† PF-Pre-fire Type( without smoke / low shrinkage/ inorganic)
† PFSH-Pre-fire Type and surface harden (without smoke / add surface strength / low shrinkage/inorganic)
1430 Ceramic Fiber Vacuum Form Shapes (RCF)
WITH ZIRCONIA
1430 Shape made from ceramic fiber bulk (Al2O3+SiO2+ZrO2), It is produced by wet vacuum forming process. After drying, finish grinding, cutting and other finishing processes to ensure the shape's precision. It has excellent mechanical properties and wind corrosion resistance, and can be directly used for thermal insulation on the hot surface and high temperature equipment.
Recommended max continuous use ≤1250ºC