5J1480
Strip
GB
Cold Drawn
Strip, Roll
Polished
Utomatic Control Devices and Instrumentation
(0.05-3.0mm)T*(>1mm)W
Bright, Printed
Can Replace Kanthal 135
Ualloy
Bimetallic Strip 5j1480
UALLOY
Rolled, Then Packed Into Plywood Pallet or Case
Hangzhou, China
7226999001
Product Description
1.2mmx 6.0mm Thermo Bimetal Strip TM-1/5J1480
Composition
Chemical composition(%)
Typical Physical properties
Composition
| Grade | 5J1480 |
| High expansion layer | Ni22Cr3 |
| Low expansion layer | Ni36 |
Chemical composition(%)
| Grade | C | Si | Mn | P | S | Ni | Cr | Cu | Fe |
| Ni36 | ≤0.05 | ≤0.3 | ≤0.6 | ≤0.02 | ≤0.02 | 35~37 | - | - | Bal. |
| Grade | C | Si | Mn | P | S | Ni | Cr | Cu | Fe |
| Ni22Cr3 | ≤0.35 | 0.15~0.3 | 0.3~0.6 | ≤0.02 | ≤0.02 | 21~23 | 2.0~4.0 | - | Bal. |
Typical Physical properties
Density (g/cm3) | 8.2 |
| Electrical resistivity at 20ºC(mm2/m) | 0.8±5% |
| Thermal conductivity, λ/ W/(m*ºC) | 22 |
| Elastic Modulus, E/ Gpa | 147~177 |
| Bending K / 10-6 ºC-1(20~135ºC) | 14.3 |
| Temperature bending rate F/(20~130ºC)10-6ºC-1 | 26.2%±5% |
| Allowable temperature (ºC) | -70~ 350 |
| Linear temperature (ºC) | -20~ 180 |